What is the KA fishing boat steel impact test

In line with the service concept of "honesty first, customer first" and the service tenet of "all for customer satisfaction", the company adopts the acceptance and response mode of combining manual and automatic, and accepts the diversified service demands of customer business consultation, complaint declaration, business acceptance, etc. through telephone, fax, e-mail, visit, letter, etc.

Low-alloy high-strength steel grades are designed to have quite good notch toughness for their intended structural use. The applicability of the notch toughness of specific grades of low-alloy high-strength steel is either based on existing use experience or combined with the results of the impact test of notched specimens. In order to meet the very strict requirements of certain applications, some KA fishing boat steel, low-alloy high-strength steels produced have excellent notch toughness. For example, controlled hot rolling technology is usually used to produce low-alloy high-strength steel plates for the manufacture of welded line pipes. Such steel pipes need to meet the requirements of relevant standards for notch toughness.

Asme sa514 grade B quenched and tempered alloy steel element composition%
C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.70-1.00, P max.: 0.035, S max.: 0.035, B max.: 0.005, Cr: 0.40-0.65, Mo: 0.15-0.25, V: 0.03-0.08, Ti: 0.01-0.03
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

If customers have any difficult problems during use of the steel materials, they can contact the company's after-sales service department to feedback the existing problems. The after-sales department will reply as soon as possible to ensure that each customer has a good after-sales experience. Under special circumstances, the after-sales service department will start the problem-solving process, and the engineers in charge of the area will quickly follow up to solve the problem.