High strength steel Q345B, GB/T 1591-2008 Q345B steel size and stock (mm): 7*2200*6500, 15*1050*8000, 5.5*3000*3600, 15*2200*3650, 32*1800*0000, 7*1600*6000, 28.5*3240*5700, 43.5*1630*3900, 23*2980*3500, 46*750*11300, 6*1460*6000, 10*2500*10000, 40*1770*3350, 26*1830*3500, 26*1800*2800, 11*2890*2880, 26*1300*11000, 43.5*1600*3900, 14*2000*3100, 11*2800*3250, 36*1100*8650, 23.4*2280*2800.
The company has TMCP CCS EH32 engineering ships steel advanced production equipment and machining technology, excellent marketing team and domestic regional channel partners, and sound management plan for product market development and after-sales service. After years of cooperation experience TMCP CCS EH32 engineering ships steel, we have accumulated a large number of customers at home and abroad, and won unanimous praise.
S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the TMCP CCS EH32 engineering ships steel rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of TMCP CCS EH32 engineering ships steel steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.
Laser cutting is that the horizontal laser beam emitted by the laser changes into a vertical downward laser beam through the 45° total reflector, and then focuses through the lens, forming a tiny spot at the focal point. When the spot hits the material, the material is heated to the vaporization temperature quickly, and evaporates to form a hole. With the movement of the beam on the material such as TMCP CCS EH32 engineering ships steel, the auxiliary gas (carbon dioxide gas, oxygen, Nitrogen, etc.) blow away the melted slag, make the hole continuously form a very narrow width (such as about 0.1mm) cutting seam, and complete the cutting of materials.
The after-sale service of iron and steel products includes after-sale tracking service, technical guidance, transfer of relevant bills, handling of objections and many other contents. The handling of quality objections accounts for a large proportion. When dealing with these problems, we should distinguish the responsibilities, and compensate or return the inconvenience or loss caused to users due to steel.
Leave a Message