The company has allocated special environmental protection facilities for all A131 DH40 oil platform steel plate pollution sources, strengthened the recycling of waste resources and improved the efficiency of resource utilization. At present, the recovery and utilization rate of solid wastes such as iron slag, steel slag, iron bearing dust, A131 DH40 oil platform steel plate steel mill scale, environmental protection dust has reached 100%.
Welded steel pipe refers to the steel pipe with a joint on the surface which is welded after the steel strip or steel plate is bent and deformed into circular, square and other expected shapes. According to different welding methods, it can be divided into arc welded pipe, high frequency or low frequency resistance welded pipe, gas welded pipe, furnace welded pipe, Bondi pipe, A131 DH40 oil platform steel plate, etc. According to the weld shape, it can be divided into straight welded pipe and spiral welded pipe. Electric welded steel pipes are mainly used in oil drilling and production, machinery manufacturing, etc.; furnace welded pipes can be used as water gas pipes, large-diameter straight seam welded pipes for high-pressure oil-gas transmission, etc.; spiral welded pipes are used for oil-gas transmission, pipe piles, piers, etc. Welded steel pipe has lower cost and higher production efficiency than seamless steel pipe.
Compared with ordinary steel, the A131 DH40 oil platform steel plate special steel has the following characteristics. First, the special steel has better physical properties, higher strength, stronger compressive strength, and better precision. Second, the special steel has better chemical properties, such as high temperature resistance, low temperature resistance and corrosion resistance. Third, the composition of the special steel is more diversified, which can be synthesized by integrating other elements, such as alloy steel, high carbon steel, etc. Fourth, special steel is more flexible for processing.
S355J2 steel plate rolling process is controlled rolling process. In the rolling process, the ingot rolling temperature is 1000-1050℃; in the first stage, the low-speed and large reduction rolling process is adopted, the high-temperature stage is 950-1000℃, the A131 DH40 oil platform steel plate rolling speed is 1.6-2.0m/s, the single reduction rate is 15-20%, and the cumulative reduction rate is 40-45%, so as to ensure sufficient deformation of ingot. In the first stage, the start rolling temperature is 910-930℃, and the finish rolling temperature is ≤ 870℃.As a basic building material, steel plates are currently widely used in automobiles, shipbuilding, chemical industry, aerospace and other fields. Reasonable selection of flaw detection methods to ensure the quality of A131 DH40 oil platform steel plate steel plates is of great significance to safe production. Common defects of steel plates are folding, inclusion, shrinkage, air bubbles, delamination and cracks. These problems can be discovered in time through flaw detection.
13CrMo4-5 seamless pipe is a kind of pressure resistant seamless pipe in accordance with the European standard EN 10216-2. The chemical composition of 13CrMo4-5 seamless pipe is C 0.10-0.17, Si ≤ 0.35, Mn 0.40-0.70, P ≤ 0.025, S ≤ 0.020, Cr 0.70-1.15, Ni ≤ 0.30, Mo 0.40-0.60, Al ≤ 0.04, Cu ≤ 0.03. Mechanical properties of 13CrMo4-5 seamless pipe: tensile strength: 440-590 MPa, yield strength: ≥ 290 MPa, elongation: ≥ 22%, impact energy: ≥ 40J. A131 DH40 oil platform steel plate, 13CrMo4-5 seamless pipe is used in petroleum, chemical industry, power station, boiler and so on industries.
After the order is finished, our after-sales service center will send an email to make a feedback about our steel products' quality. We have phone service every three months to remind our customers of the possible problems and collect advices or suggestions in quality and service. Upon the collection of advices or suggestions, our after-sales service will quickly make technical solutions to wipe out the customer problem.
Leave a Message